sphc钢卷边裂原因分析.pdf

SPHC钢卷边裂原因分析别程程廖力苏刚何宇明(重庆钢铁股份有限公司,重庆 401220) 摘要对重钢1780热轧线生产的SPHC钢卷出现边裂进行了分析,认为钢卷Mn/S较低,且加热炉过烧是造成边裂的主要原因。通过控制钢中Mn/S和优化轧钢加热工艺,有效减少了钢卷的边裂缺陷。关键词 SPHC钢卷边裂原因分析 Reason Analysis for Edge Crack on SPHC Strip Coil Bie Chengcheng Liao Li Su GangHe Yuming (Chongqing Iron & Steel Co. Ltd., Chongqing, 401220) Abstract It is found that the main reason of edge crack is a low content of Mn/S as well as the over-heating in rolling process, through analysis for the edge cracks exiting on the SPHC stripe coil produced by 1780 hot rolled mill of Chongqing Iron & Steel pany. As a result, edge cracks could be remarkably reduced by controlling the content of Mn/S of steel-making and optimizing the heating process of steel-rolling. Key Words SPHCstrip coil edge crack reason analysis 1前言重庆钢铁股份有限公司1780 热轧生产线(以下简称1780线)生产的SPHC冷轧基料,存在边裂现象(图1、图2)。边裂缺陷是指钢卷边缘沿长度方向的单侧或两侧出现破裂呈裂口状,一般情况下边裂缺陷集中于钢卷的头尾部分,严重的钢卷边部全长均呈锯齿状。热轧边裂对冷轧影响很大,容易出现断带等质量事故。2013年1季度,检验冷轧基料11046卷,边裂112卷,%,缺陷钢卷对公司造成较大的经济损失,影响合同兑现,同时对用户的后续使用产生不良的影响。本文探寻了钢卷产生缺陷的原因,通过调整化学成分和热轧工艺参数,在一定程度上减少了钢卷的开裂现象。图1 边裂形貌图2 缺陷试样形貌 2边裂原因 化学成分表3列出三炉缺陷卷的化学成分,并与2013年生产的605炉同牌号平均成分相比较,两者对比如表3 所示。表3 冷轧基料缺陷钢卷成分对比表钢卷号板坯号钢号 C碳 Si硅 Mn锰 P磷 S硫 Mn/S H131839490 33F01823B708 AFT708 H132384970 33I07514A708 AFT708 H132366150 33I07613A708 AFT708 2013年该