防水板焊接工艺试验报告.doc

防水板焊接工艺试验报告防水板工艺试验批准:审核:编制:目录一、施工准备·······································································1二、焊接方法简介·································································2三、工艺流程·······································································2四、质量标准及质量检验························································2五、施工注意事项·································································34··附:焊工上岗证、防水板合格证及检测报告及工艺性试验过程照片EVA防水板焊接工艺试验报告一、施工准备1、材料其产品合格证和检测报告。×3m)及EVA防水板2块(、设备注射针、压力表、打气5#(GIT-810)双焊缝温控热熔爬焊机、手持温控热熔焊枪、筒等。双焊缝温控热熔爬焊机参数如下:(V)220V输入电压(HZ)50Hz频率(W)800W功率5m~焊接速度(m/min))0~450℃加热温度(℃(mm)~15cm搭接宽度(cm)10cm~85%母材(剪切方向抗拉)焊缝强度≥(Kg)5整机重量类绝缘等级II、作业条件3(1)焊工有考试合格证。)防水板搭接符合规定(10mm)。(2正弦交流电。3()电源220V触电、防火和必要的通风措施,放止发生烧伤、作业场地要有安全防护设施、4()中毒及火灾等事故。页1第4、主要的参数有:焊接速度、焊接温度等。二、焊接方法简介防水板焊接是防水施工中的关键工序,对能否有效防水起着决定性作用。我标段防水板焊接采用热熔焊接。热熔焊接是通过加热的方法使两块搭接在一起的防水板热融后相互对接融合,经冷却固定连接在一起的方法。一、应用范围此方法焊接性能优良,操作方便,焊接速度高,焊接质量好。广泛应用于高速公路、隧道、桥梁,水库、建筑、人工湖、桥梁、游泳池、养殖池等防水工程。二、热熔焊的特点(1)温度控制精确,稳定。(2)运行受外界电源波动影响小,爬行比较平稳。三、工艺流程1、检查设备→选择焊接参数→施焊→质量检验→确定焊接参数。2、检查电源、焊机及压力表等工具。焊机在焊接过程中速度要保持平稳,防止因过快或过慢导致漏焊、焊焦或焊穿。3、选择焊接参数。根据以往经验,选择4m/min的焊接速度,温度为:350℃。5、施焊操作。将焊机在搭接好的防水板上调试好后,开始焊接。焊缝宽度16mm、17mm,搭接宽度不小于100mm,焊接均匀连续,无假焊、漏焊、焊焦、焊穿等现象。焊接完毕后,用手持温控热熔焊枪将试件两端焊封闭,最后进行焊接质量检验。四、质量标准及质量检验1、检验标准焊接完毕后采用检漏器进行充气检测,,保持该压力不少于5分钟,允许压力下降20%。如压力持续下降,应查出漏气部位并对漏气部位进行全面的手工补焊。页2第2、检验方法将5号注射针与压力表相连,将注射针直接插入中